3Cr13 2Cr13 1Cr13 Bearing seamless steel tube
Quick info:
| Material | 3Cr13 2Cr13 1Cr13 |
| OD | 4-440mm |
| WT | 2-50mm |
| Production Method | Seamless+Cold draw or Cold rolled |
| Application | Used for washing machine shaft sleeve,Bearing sleeve |
| End | Plain |
| Standard | ASTM A519 EN10305-1 DIN 2391 etc |
Detail info:
Material Feature:
1cr13, 2cr13, 3cr13 belong to martensitic stainless steel, the main difference is that the carbon content is different:
The carbon content of 1Cr13 is 0.15%, 2Cr13 is 0.16-0.25% and 3Cr13 is 0.26-0.35%.
1cr13, 2cr13, can not be quenched directly, 3cr13 can be quenched directly.
1Cr13 semi-martensitic section steel has high strength, toughness, good corrosion resistance and machinability after quenching and tempering. It is mainly used for parts requiring high toughness, certain stainless property and bearing impact load, such as blades, fasteners, hydraulic press valves, thermal cracking anti-sulfur corrosion equipment, etc. It can also be used for equipment with weak corrosion resistance at room temperature and component 2Cr13 with high hardness and good corrosion resistance under quenching condition. It can be used for steam turbine blades.
3Cr13 is used as cutting tool, nozzle, valve seat, valve, etc. It has higher carbon content than 1Cr13 and 2Cr13 steels, so it has higher strength, hardness and hardenability. However, the corrosion resistance and thermal stability of the steel below 700 C are lower than those of 1Cr13 and 2Cr13, and the weldability of the steel is poor. It is used to manufacture structural parts with high strength, wear parts under high stress mechanical loads and some corrosive media, such as cutters and springs working below 300 C, axles, bolts, valves, bearings, seat and nozzles working below 400 C, etc. It is also used to manufacture measuring instruments and medical tools.
Production method:
Seamless+Cold draw or Cold rolled,Control good tolerance of tubes by cold draw to meet customer's requests.
QUALITY CONTROL:
1. Incoming Raw Material Inspection
2. Raw Material Segregation to avoid steel grade mix-up
3. Heating and Hammering End for Cold Drawing
4. Cold Drawing and Cold Rolling, on line inspection
5. Heat Treatment, +A, +SRA, +LC, +N, Q+T
6. Straightening-Cutting to specified length-Finished Measuring Inspection
7. Machanical Testing in own labs with Tensile Strength, Yield Strength, Elongation, Hardness, Impact, Mictrostruture etc
8. Packing and Stocking
100% of our steel tubes are dimensionally checked
100% of our steel tubes are visually checked to assure they have a perfect surface condition and no surface defects.
100% eddy current test and ultrosonic test to eliminate longitudinal and transversal defects.